Article Title: Prolonged UV-C Irradiation is a Double-Edged Sword on the Zirconia Surface

doi: 10.1021/acsomega.9b04123

Figure Lengend Snippet: Treatment Conditions of the Zirconia Samples in Different Groups (NA = Not Applicable)

Article Snippet: UV-A irradiation (UV fluorescence cabinet CL 150, SPECTROLINE, Westbury, New York, USA) was 365 nm in wavelength and 550 μW cm –2 in intensity, whereas UV-C irradiation (UV fluorescence cabinet CL 150, SPECTROLINE, Westbury, New York, USA) was 243 nm in wavelength and 490 μW cm –2 in intensity.

Techniques: Irradiation, Control

Journal: Royal Society Open Science

Article Title: Modifying cellulose fibres with carbon dots: a promising approach for the development of antimicrobial fibres

doi: 10.1098/rsos.231755

Figure Lengend Snippet: Absorption and emission properties of the CDs. Absorption and emission spectra of ( a ) BACDs and ( b ) PBA-CCMCDs. The absorption profiles of the CDs in the wavelength range of 200–500 nm are represented by the red plots. BACDs exhibited two absorption peaks at 268 nm and 329 nm ( a , red plot). PBA-CCMCDs showed a single peak at 317 nm ( b , red plot). The fluorescence properties of the CDs were analysed by recording their emission spectra with the aqueous solutions of the CDs in PBS excited at 270 nm (BACDs) and 315 nm (PBA-CCMCDs).

Article Snippet: For UV treatment, the plates were exposed to UV light (5 W) for 90–120 min inside a Fluorescence Analysis cabinet (Spectroline, USA) using 365 nm longwave UV light at a distance of approximately 8 cm from the top surface of the plate.

Techniques: Fluorescence

Journal: ACS Omega

Article Title: Prolonged UV-C Irradiation is a Double-Edged Sword on the Zirconia Surface

doi: 10.1021/acsomega.9b04123

Figure Lengend Snippet: Zirconia samples irradiated with UV-A or UV-C with respect to different times (15 min, 3 and 24 h). NB: UV-C irradiation caused color changes in the samples. SEM images of surface morphology and EDX analysis.

Article Snippet: UV-A irradiation (UV fluorescence cabinet CL 150, SPECTROLINE, Westbury, New York, USA) was 365 nm in wavelength and 550 μW cm –2 in intensity, whereas UV-C irradiation (UV fluorescence cabinet CL 150, SPECTROLINE, Westbury, New York, USA) was 243 nm in wavelength and 490 μW cm –2 in intensity.

Techniques: Irradiation

Journal: ACS Omega

Article Title: Prolonged UV-C Irradiation is a Double-Edged Sword on the Zirconia Surface

doi: 10.1021/acsomega.9b04123

Figure Lengend Snippet: Treatment Conditions of the Zirconia Samples in Different Groups (NA = Not Applicable)

Article Snippet: UV-A irradiation (UV fluorescence cabinet CL 150, SPECTROLINE, Westbury, New York, USA) was 365 nm in wavelength and 550 μW cm –2 in intensity, whereas UV-C irradiation (UV fluorescence cabinet CL 150, SPECTROLINE, Westbury, New York, USA) was 243 nm in wavelength and 490 μW cm –2 in intensity.

Techniques: Irradiation